LEXAN 243R
原厂原包供应Lexan PC 243R物性表
熔体流动速率MFR：10.5。紫外稳定。改良的阻燃性能。内含脱模剂
SABIC沙伯基础创新Lexan PC 243R中英文物性表资料
SABIC Innovative Plastics Lexan® 243R PC
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source! | |
Material Notes: |
LEXAN 243R is a medium viscosity multi purpose UV stabilized grade and contains release agent to ensure easy processing. This grade is UL94-V2 at 0.8 mm approved. |
Physical Properties物理性质 |
Metric公制数据 |
English英制数据 |
Comments测试方法 |
Density密度 |
1.20 g/cc |
0.0434 lb/in³ |
ISO 1183 |
Moisture Absorption at Equilibrium吸湿平衡 |
0.15 % |
0.15 % |
23°C / 50% RH; ISO 62 |
Water Absorption at Saturation吸水率 |
0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
Linear Mold Shrinkage, Flow线性收缩率/流动 |
0.0050 - 0.0070 cm/cm |
0.0050 - 0.0070 in/in |
on tensile bar; SABIC Method |
Melt Flow熔体流动速率 |
12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
Mechanical Properties力学性能 |
Metric公制数据 |
English英制数据 |
Comments测试方法 |
Hardness,硬度 H358/30 |
95.0 MPa |
13800 psi |
ISO 2039-1 |
Tensile Strength at Break断裂拉伸强度 |
70.0 MPa |
10200 psi |
50 mm/min; ISO 527 |
Tensile Strength, Yield屈服拉伸强度 |
63.0 MPa |
9140 psi |
50 mm/min; ISO 527 |
Elongation at Break断裂伸长率 |
110 % |
110 % |
50 mm/min; ISO 527 |
Elongation at Yield屈服伸长率 |
6.0 % |
6.0 % |
50 mm/min; ISO 527 |
Tensile Modulus拉伸模量 |
2.35 GPa |
341 ksi |
1 mm/min; ISO 527 |
Flexural Yield Strength弯曲屈服强度 |
90.0 MPa |
13100 psi |
2 mm/min; ISO 178 |
Flexural Modulus弯曲弹性模量 |
2.30 GPa |
334 ksi |
2 mm/min; ISO 178 |
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO) |
12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO) |
NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
Charpy Impact Unnotched夏比缺口试样冲击 |
NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched夏比缺口冲击 |
1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C | |
7.30 J/cm² @Temperature 23.0 °C |
34.7 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗 |
10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; SABIC Method |
Electrical Properties电性能 |
Metric公制数据 |
English英制数据 |
Comments测试方法 |
Volume Resistivity体积电阻率 |
>= 1.00e+15 ohm-cm |
>= 1.00e+15 ohm-cm |
IEC 60093 |
Surface Resistance表面电阻 |
>= 1.00e+15 ohm |
>= 1.00e+15 ohm |
ROA; IEC 60093 |
Dielectric Constant介电常数 |
2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
Dielectric Strength介电强度 |
15.0 kV/mm @Thickness 1.00 mm |
381 kV/in @Thickness 0.0394 in |
short time; IEC 60243-1 |
17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
Dissipation Factor耗散因数 |
0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
Thermal Properties热性能 |
Metric公制数据 |
English英制数据 |
Comments测试方法 |
CTE, linear, Parallel to Flow线性热膨胀系数 |
70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
Thermal Conductivity导热系数 |
0.200 W/m-K |
1.39 BTU-in/hr-ft²-°F |
ISO 8302 |
Deflection Temperature at热变形温度 0.46 MPa (66 psi) |
136 °C |
277 °F |
Edgew 120*10*4 sp=100mm; ISO 75/Be |
Deflection Temperature at热变形温度 1.8 MPa (264 psi) |
125 °C |
257 °F |
Edgew 120*10*4 sp=100mm; ISO 75/Ae |
Vicat Softening Point维卡软化点 |
141 °C |
286 °F |
Rate B/50; ISO 306 |
142 °C |
288 °F |
Rate B/120; ISO 306 | |
153 °C |
307 °F |
Rate A/50; ISO 306 | |
UL RTI, Electrical相对温度指数 |
130 °C |
266 °F |
UL 746B |
UL RTI, Mechanical with Impact机械冲击热指数 |
125 °C |
257 °F |
UL 746B |
UL RTI, Mechanical without Impact无机械冲击热指数 |
125 °C |
257 °F |
UL 746B |
Flammability, UL94阻燃等级 |
V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
UL 94 |
V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
UL 94 | |
Oxygen Index氧指数 |
25 % |
25 % |
LOI; ISO 4589 |
Glow Wire Test灼热丝测试 |
850 °C @Thickness 1.00 mm |
1560 °F @Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
Optical Properties光学性质 |
Metric公制数据 |
English英制数据 |
Comments测试方法 |
Refractive Index折射率 |
1.586 |
1.586 |
ISO 489 |
Haze雾度 |
<= 0.80 % @Thickness 2.54 mm |
<= 0.80 % @Thickness 0.100 in |
ASTM D 1003 |
Transmission, Visible透光率 |
88 - 90 % @Thickness 2.54 mm |
88 - 90 % @Thickness 0.100 in |
ASTM D 1003 |
以下是沙特-SABIC塑料LEXAN PC 243R物性表参数